| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.938 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.057 | g/10min | |
| 薄膜 | SecantModulus-MD(13µm) | ASTMD882 | 641 | MPa | |
| 薄膜 | SecantModulus-TD(13µm) | ASTMD882 | 772 | MPa | |
| 薄膜 | TensileStrength-MD(Yield,13µm) | ASTMD882 | 26.3 | MPa | |
| 薄膜 | TensileStrength-TD(Yield,13µm) | ASTMD882 | 23.1 | MPa | |
| 薄膜 | TensileStrength-MD(Break,13µm) | ASTMD882 | 88.3 | MPa | |
| 薄膜 | TensileStrength-TD(Break,13µm) | ASTMD882 | 47.5 | MPa | |
| 薄膜 | TensileElongation-MD(Break,13µm) | ASTMD882 | 270 | % | |
| 薄膜 | TensileElongation-TD(Break,13µm) | ASTMD882 | 390 | % | |
| 薄膜 | TotalEnergyImpact | 13µm | ASTMD4272 | 3.12 | J |
| 薄膜 | TotalEnergyImpact | 100µm | ASTMD4272 | 5.97 | J |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 13µm | ASTMD1922 | 20 | g |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 100µm | ASTMD1922 | 420 | g |
| 薄膜 | ElmendorfTearStrength-TD | 13µm | ASTMD1922 | 40 | g |
| 薄膜 | ElmendorfTearStrength-TD | 100µm | ASTMD1922 | 750 | g |