| 规格级别 | 丁烯共聚单体,抗氧化性,可加工性，良好,食品接触的合规性,低速凝固晶点 薄膜挤出 | 外观颜色 | |
| 该料用途 | 薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.936 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.72 | g/10min | |
| 机械性能 | 摩擦系数(吹塑薄膜) | ASTMD1894 | 0.24 | ||
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD(38µm,BlownFilm) | ASTMD882 | 390 | MPa | |
| 薄膜 | SecantModulus-1%Secant,TD(38µm,BlownFilm) | ASTMD882 | 520 | MPa | |
| 薄膜 | TensileStrength-MD(Yield,38µm,BlownFilm) | ASTMD882 | 17.0 | MPa | |
| 薄膜 | TensileStrength-TD(Yield,38µm,BlownFilm) | ASTMD882 | 17.0 | MPa | |
| 薄膜 | TensileStrength-MD(Break,38µm,BlownFilm) | ASTMD882 | 34.0 | MPa | |
| 薄膜 | TensileStrength-TD(Break,38µm,BlownFilm) | ASTMD882 | 29.0 | MPa | |
| 薄膜 | TensileElongation-MD(Break,38µm,BlownFilm) | ASTMD882 | 600 | % | |
| 薄膜 | TensileElongation-TD(Break,38µm,BlownFilm) | ASTMD882 | 900 | % | |
| 薄膜 | 落锤冲击(38µm,吹塑薄膜) | ASTMD1709A | 62 | g | |
| 薄膜 | ElmendorfTearStrength-MD(38µm,BlownFilm) | ASTMD1922 | 40 | g | |
| 薄膜 | 埃尔曼多夫抗撕强度-TD(38µm,吹塑薄膜) | ASTMD1922 | 130 | g | |
| 薄膜 | OxygenPermeability2(23°C,38µm,BlownFilm) | ASTMD1434 | 2300 | cm³/m²/24hr | |
| 薄膜 | WaterVaporTransmissionRate(38°C,100%RH,38µm,BlownFilm) | 5.2 | g/m²/24hr | ||
| 热性能 | 脆化温度 | ASTMD746 | -70.0 | °C | |
| ADDITIONAL INFORMATION | 补充信息 | TestMethod | NominalValue | Unit | |
| ADDITIONAL INFORMATION | LowFrictionPuncture-BlownFilm(38.0µm) | InternalMethod | 240 | J/cm | |