| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | 手袋 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.925 | g/cm3 | |
| 基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min |
| 机械性能 | 摩擦系数 | Blown Film | ASTM D-1894 | 0.12 | |
| 机械性能 | 摩擦系数 | Blown Film | ASTM D-1894 | 0.14 | |
| 机械性能 | 薄膜厚度-Tested | 50 | um | ||
| 机械性能 | 薄膜厚度-Tested | 100 | um | ||
| 机械性能 | 割线模量-2% Secant(MD) | 50um | ASTM D-882 | 230 | MPa |
| 机械性能 | 割线模量-2% Secant(TD) | 50um | ASTM D-882 | 240 | MPa |
| 机械性能 | 割线模量-2% Secant(TD) | 100um | ASTM D-882 | 220 | MPa |
| 机械性能 | 割线模量-2% Secant(MD) | 100um | ASTM D-882 | 210 | MPa |
| 机械性能 | 拉伸屈服强度(MD) | 50um | ASTM D-882 | 10 | MPa |
| 机械性能 | 拉伸屈服强度(TD) | 50um | ASTM D-882 | 12 | MPa |
| 机械性能 | 拉伸屈服强度(MD) | 100um | ASTM D-882 | 10 | MPa |
| 机械性能 | 拉伸屈服强度(TD) | 100um | ASTM D-882 | 12 | MPa |
| 机械性能 | 拉伸断裂强度(MD) | 50um | ASTM D-882 | 32 | MPa |
| 机械性能 | 拉伸断裂强度(TD) | 50um | ASTM D-882 | 32 | MPa |
| 机械性能 | 拉伸断裂强度(MD) | 100um | ASTM D-882 | 30 | MPa |
| 机械性能 | 拉伸断裂强度(TD) | 100um | ASTM D-882 | 23 | MPa |
| 机械性能 | 拉伸断裂伸长率(TD) | 50um | ASTM D-882 | 1000 | % |
| 机械性能 | 拉伸断裂伸长率(MD) | 50um | ASTM D-882 | 1000 | % |
| 机械性能 | 拉伸断裂伸长率(MD) | 100um | ASTM D-882 | 750 | % |
| 机械性能 | 拉伸断裂伸长率(TD) | 100um | ASTM D-882 | 800 | % |
| 机械性能 | 落锤冲击 | 50um | ASTM D-1709 | 240 | g |
| 机械性能 | 落锤冲击 | 100um | ASTM D-1709 | 140 | g |
| 机械性能 | 埃尔曼多夫撕裂强度(MD) | 50um | ASTM D-1922 | 630 | g |
| 机械性能 | 埃尔曼多夫撕裂强度(TD) | 50um | ASTM D-1922 | 1100 | g |
| 机械性能 | 埃尔曼多夫撕裂强度(TD) | 100um | ASTM D-1922 | 520 | g |
| 机械性能 | 埃尔曼多夫撕裂强度(MD) | 100um | ASTM D-1922 | 290 | |
| 光学性能 | 光泽度 | 50um | ASTM D-2457 | 66 | |
| 光学性能 | 光泽度 | 100um | ASTM D-2457 | 68 | |
| 光学性能 | 雾度 | 50um | ASTM D-1003 | 12 | % |
| 光学性能 | 雾度 | 100um | ASTM D-1003 | 8 | % |