| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.919 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 1.0 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | ASTMD746 | 50 | µm | |
| 薄膜 | 抗张强度 | MD:屈服 | ASTMD882 | 11.3 | MPa |
| 薄膜 | 抗张强度 | TD:屈服 | ASTMD882 | 10.3 | MPa |
| 薄膜 | 抗张强度 | MD:断裂 | ASTMD882 | 41.2 | MPa |
| 薄膜 | 抗张强度 | TD:断裂 | ASTMD882 | 34.3 | MPa |
| 薄膜 | 伸长率 | MD:断裂 | ASTMD882 | 750 | % |
| 薄膜 | 伸长率 | TD:断裂 | ASTMD882 | 850 | % |
| 薄膜 | ElmendorfTearStrength | MD | ASTMD1922 | 63.7 | kN/m |
| 薄膜 | ElmendorfTearStrength | TD | ASTMD1922 | 127.5 | kN/m |
| 薄膜 | SpencerImpact | ASTMD3420 | 1.18 | J | |
| 薄膜 | 薄膜厚度-经测试 | ASTMD746 | 50 | µm | |
| 薄膜 | 抗张强度 | MD:屈服 | ASTMD882 | 11.3 | MPa |
| 薄膜 | 抗张强度 | TD:屈服 | ASTMD882 | 10.3 | MPa |
| 薄膜 | 抗张强度 | MD:断裂 | ASTMD882 | 41.2 | MPa |
| 薄膜 | 抗张强度 | TD:断裂 | ASTMD882 | 34.3 | MPa |
| 薄膜 | 伸长率 | MD:断裂 | ASTMD882 | 750 | % |
| 薄膜 | 伸长率 | TD:断裂 | ASTMD882 | 850 | % |
| 薄膜 | ElmendorfTearStrength | MD | ASTMD1922 | 63.7 | kN/m |
| 薄膜 | ElmendorfTearStrength | TD | ASTMD1922 | 127.5 | kN/m |
| 薄膜 | SpencerImpact | ASTMD3420 | 1.18 | J | |
| 热性能 | 维卡软化温度 | ASTMD1525 | 100 | °C | |
| 光学性能 | 雾度 | ASTMD1003 | 17 | % | |